CERAMIC FIBER BOARD is made of high purity alumina fibrous and alumina powder,to be formed and fired in special equipment with advanced patent process,can withstand temperature up to 1700 celsius.
| Type | BR-1000 | BR-1260 | BR-1400 | BR-1600 | BR-1700 | BR-1800 |
| Classification temperature | 1000 | 1260 | 1400 | 1600 | 1700 | 1800 |
| density (Kg/m3) | 200-600 | 200-600 | 200-600 | 200-600 | 350-600 | 350-600 |
| Line change(.CX24hS) | 1.3 (900.C) | 1.1 (1100.C) | 1.6 (1200.C) | <2.0 (1400.C) | <2.0 (1500.C) | <2.0 (1600.C) |
| compressive strength | 0.5 | 0.5 | 0.5 | 0.3 | 0.3 | 0.3 |
| Density(Kg/m3) | 400 | |
| Strength to resist bending(MPa,25.C) | 0.72 | |
| Linear shrinkage rate % (1600 .Cx8hrs) | 0.13(1.7)* | |
| Expansion rate at %(600.C) | 0.28 | |
| Average modulus of linear expansion (x10-6/K) | 1.77 | |
| Thermal conductivity rate GHP[W/(mK)] |
400.C | 0.147 |
| 600.C | 0.186 | |
| 800.C | 0.236 | |
| 1000.C | 0.296 | |
| Chemical composition | AL2O3:87% SiO2:13% | |
25x600x900mm
40x600x900mm
30x600x900mm
50x600x900mm
100x600x900mm
| Character | product applying |
| High-temperature steady | Verity high-temperature industrial furnace backing heat insulation |
| low heat conductivity | Ceramics kiln, mechanic and metallurgy heating furnace, thermal treatment furnace and others industrial furnace and hot face internal lining Low heating quantity High-temperature block-fire and flame-insulated |
| easy-mechanic processing | Kiln door, kiln car and dilatation joint etc insulation material |
| Tidy surface | Glass kiln insulation |